ALUMINUM ALLOY FOIL FOR ELECTRODE CURRENT COLLECTORS AND MANUFACTURING METHOD THEREOF

It is an object to provide an aluminum alloy foil for an electrode current collector, the foil having a high post-drying strength after application of an active material while keeping a high electrical conductivity. Disclosed is an aluminum alloy foil for an electrode current collector, comprising 0.1 to 1.0 mass% (hereinafter, "mass%" is simply referred to as "%") of Fe, 0.01 to 0.5% of Si, and 0.01 to 0.2% of Cu, with the rest consisting of A1 and unavoidable impurities, wherein the aluminum alloy foil after final cold rolling has a tensile strength of 220 MPa or higher, a 0.2% yield strength of 180 MPa or higher, and an electrical conductivity of 58% IACS or higher; and the aluminum ally foil has a tensile strength of 190 MPa or higher and a 0.2% yield strength of 160 MPa or higher even after the aluminum alloy foil is subjected to heat treatment at any of 120°C for 24 hours, 140°C for 3 hours, and 160°C for 15 minutes.