METHOD FOR PREPARING UNIFORMLY-CURED SOLID LOADING TIRES FROM HIGH-MODULUS GRAPHENE OXIDE/NATURAL RUBBER COMPOSITE

A method for preparing a uniformly-cured solid loading tire from a high-modulus graphene oxide/natural rubber composite is provided. A high-modulus graphene oxide/carbon black/natural rubber mixture sheet and two high-viscosity graphene oxide/carbon black/natural rubber mixture sheets are prepared, where a weight ratio of graphene oxide to natural rubber to carbon black to an interface modifying agent to an anti-aging agent to an antioxidant to a vulcanization accelerator to an activator to a softener to a vulcanizing agent is 0.5-5:100:40-120:1-20:1-10:1-10:1-20:1-20:1-20:1-20. The high-modulus rubber mixture sheet is sandwiched between the two high-viscosity rubber mixture sheets to form a sandwich-structure rubber mixture laminate, which is then processed into a strip. The strip is wound along a surface of a hub of a loading wheel, and then the hub is transferred to a mold for vulcanization to obtain the desired tire.